Development of thermal barrier coating systems from Al microparticles. Part I: Influence of processing conditions on the mechanisms of formation - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Surface and Coatings Technology Année : 2019

Development of thermal barrier coating systems from Al microparticles. Part I: Influence of processing conditions on the mechanisms of formation

Résumé

This work presents the mechanisms of formation on pure nickel of full thermal barrier coating systems (aluminide coating, thermally grown oxide and thermal barrier top coating) from micro-sized Al particles dispersed in a slurry annealed in different atmospheres (Ar, synthetic air, water vapour and mixtures thereof). The simultaneous formation of nickel aluminides and of a thermal barrier made of sintered hollow alumina spheres involved self-propagating high-temperature synthesis in all conditions. However, the microstructures and adherence of the top coatings changed markedly with either a diffusion step (700°C-2 h) or a complete heat treatment (700°C-2 h + 1100°C-2 h) depending on the atmosphere. Whereas fast consumption of Al occurred in Ar to form the nickel aluminides, synthetic air and water vapour fostered the peripheral oxidation of Al micro-sized particles that impeded the release of Al and its diffusion towards the substrate. This resulted in heterogeneous diffusion layers but thicker top coatings with better sintering and thicker alumina shells.

Domaines

Matériaux
Fichier principal
Vignette du fichier
Development of thermal barrier coating systems from Al microparticles-Part 1_to share.pdf (2.42 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02542049 , version 1 (14-04-2020)

Identifiants

Citer

Germain Boissonnet, Benjamin Grégoire, Gilles Bonnet, Fernando Pedraza. Development of thermal barrier coating systems from Al microparticles. Part I: Influence of processing conditions on the mechanisms of formation. Surface and Coatings Technology, 2019, 380, pp.125085. ⟨10.1016/j.surfcoat.2019.125085⟩. ⟨hal-02542049⟩
60 Consultations
148 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More