Aluminum substitution for vanadium in the Na3V2(PO4 )2F3 and Na3V2(PO4)2FO2 type materials

Résumé

Among the positive electrode materials for Na-ion batteries, Na3V2(PO4)2F3 is considered as one of the most promising and generates high interest. Here, we study the influence of the sol–gel synthesis parameters on the structure and on the electrochemical signature of the partially substituted Na3V2−zAlz(PO4)2(F,O)3 materials. We demonstrate that the acidity of the starting solution influences the vanadium oxidation state of the final product. For the first time we report on the possibility of controlling the double Al/V and O/F substitution that leads to the preparation of the Na3V2−zAlz(PO4)2F1+zO2−z solid solution.

Domaines

Fichier principal
Vignette du fichier
2019-128.pdf (1.05 Mo) Télécharger le fichier
Vignette du fichier
2019-128-suppl_mater.pdf (968.58 Ko) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)
Licence
Format Figure, Image
Licence

Dates et versions

hal-02294384 , version 1 (04-10-2019)

Licence

Identifiants

Citer

Jacob Olchowka, Long H. B. Nguyen, Thibault Broux, Paula Sanz Camacho, Emmanuel Petit, et al.. Aluminum substitution for vanadium in the Na3V2(PO4 )2F3 and Na3V2(PO4)2FO2 type materials. Chemical Communications, 2019, 55 (78), pp.11719-11722. ⟨10.1039/C9CC05137F⟩. ⟨hal-02294384⟩
243 Consultations
622 Téléchargements

Altmetric

Partager

  • More