Microstructural characteristics and corrosion resistance of atmospheric pressure chemical vapor deposited SiO2 films from TEOS and O2 - Archive ouverte HAL Accéder directement au contenu
Communication Dans Un Congrès Année : 2018

Microstructural characteristics and corrosion resistance of atmospheric pressure chemical vapor deposited SiO2 films from TEOS and O2

Résumé

Chemical vapor deposited SiO2 films from tetraethyl orthosilicate (TEOS) is a key enabling material in numerous applications. Among the several pathways for the CVD of SiO2 films from TEOS, the poorly investigated medium temperature process involving oxygen ensures a compromise between the high thermal load of the surface reaction of the TEOS pyrolysis process, and the strong activation of gas phase reactions in the ozone assisted decomposition of TEOS. It is a promising route towards conformal coverage of complex-in-shape structures, growth rate control, and appropriate physical & chemical properties of the coating. SiOx films are obtained from TEOS+O2 in a horizontal CVD reactor operating at atmospheric pressure between 350 and 500°C. FTIR operating under normal and 55° incidence angle is used for the investigation of the structure, namely density, strain, oxygen content and stoichiometry of the films, by probing vibrational modes in the 900-1300 cm-1 region with well-resolved TO-LO phonon splitting. Complementary density values obtained by ellipsometry allow estimating the porosity of the films. Their corrosion resistance is investigated by the P-Etch test through thickness loss and is correlated with their composition, porosity and density.
Fichier principal
Vignette du fichier
Ponton_21803.pdf (95.15 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-04382802 , version 1 (11-01-2024)

Identifiants

  • HAL Id : hal-04382802 , version 1
  • OATAO : 21803

Citer

Simon Ponton, Franck Dhainaut, Hugues Vergnes, Brigitte Caussat, Diane Samélor, et al.. Microstructural characteristics and corrosion resistance of atmospheric pressure chemical vapor deposited SiO2 films from TEOS and O2. CIMTEC 2018, Jun 2018, Perugia (Italy), Italy. ⟨hal-04382802⟩
24 Consultations
5 Téléchargements

Partager

Gmail Facebook X LinkedIn More