The growth of Ti3SiC2 coatings onto SiC by reactive chemical vapor deposition using H2 and TiCl4

Résumé

(SiC/Ti3SiC2)n multilayered coatings composed of n layers alternately of continuous SiC and Ti3SiC2 sub-layers were prepared on carbon substrates. The method consists in depositing SiC by classical chemical vapor deposition (CVD) and then producing a new Ti-containing sub-layer from a reaction between SiC and a H2/TiCl4 gaseous mixture by reactive CVD (RCVD), and repeating this sequence n times. In accordance with thermodynamics, this RCVD method produces only pure TiC sub-layers when a low dilution ratio of TiCl4 in H2 (R = [H2]/[TiCl4]) is used. With a high R value, the growth of pure Ti3SiC2 thin continuous sub-layers from solid–gas reaction is observed for short deposition times. But for long deposition times, the simultaneous growth of additional Ti5Si3Cx and TiC sub-layers occurs from solid state diffusion when the initial Ti3SiC2 sub-layer thickness exceeds about 1 μm. In that case, the repeating of the sequence results in the further conversion of the additional phases into new Ti3SiC2 sub-layers from solid state reactions involving TiSi2 as an intermediate phase and SiC.

Domaines

Chimie
Fichier principal
Vignette du fichier
Postprint for Hal - FAKIH - RCVD Ti3SiC2 - 2006.pdf (2.61 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-04260387 , version 1 (26-10-2023)

Identifiants

Citer

H. Fakih, Sylvain Jacques, M.-P. Berthet, F. Bosselet, O. Dezellus, et al.. The growth of Ti3SiC2 coatings onto SiC by reactive chemical vapor deposition using H2 and TiCl4. Surface and Coatings Technology, 2006, 201 (6), pp.3748-3755. ⟨10.1016/j.surfcoat.2006.09.040⟩. ⟨hal-04260387⟩
13 Consultations
13 Téléchargements

Altmetric

Partager

Gmail Mastodon Facebook X LinkedIn More