Oxidation of Ni-Cr alloy at intermediate oxygen pressures. II. Towards the lifetime prediction of alloys - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Corrosion Science Année : 2016

Oxidation of Ni-Cr alloy at intermediate oxygen pressures. II. Towards the lifetime prediction of alloys

Eric Schmucker
  • Fonction : Auteur correspondant
  • PersonId : 1234890
  • IdRef : 200020242

Connectez-vous pour contacter l'auteur
Carine Petitjean
Pierre-Jean Panteix
Sabah Ben Lagha
  • Fonction : Auteur
Michel Vilasi

Résumé

The formation of protective Cr 2 O 3 layer on Ni-Cr alloys depends on (i) the chromium concentration at the alloy/oxide interface and (ii) the chromium diffusion in the alloy from the core towards the surface. A sufficient interfacial chromium content and chromium gradient are necessary to sustain the selective external oxidation of chromium. Ni-30Cr samples have been oxidised at 1150 • C in 10 −13 up to 10 −3 atm O 2. Analytical methods are used to model the diffusion in steady-state conditions and to predict the lifetime of the alloy. The interdiffusion coefficient is found equal to 1.2 × 10 −10 cm 2 s −1 .
Fichier principal
Vignette du fichier
Révision - Article II - Oxidation of Ni-Cr_LM HAL.pdf (917.17 Ko) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-04019254 , version 1 (08-03-2023)

Identifiants

Citer

Eric Schmucker, Carine Petitjean, Laure Martinelli, Pierre-Jean Panteix, Sabah Ben Lagha, et al.. Oxidation of Ni-Cr alloy at intermediate oxygen pressures. II. Towards the lifetime prediction of alloys. Corrosion Science, 2016, 111, pp.467-473. ⟨10.1016/j.corsci.2016.05.024⟩. ⟨hal-04019254⟩