Diffusion Bonding of Al7075 to Ti-6Al-4V by Spark Plasma Sintering and Using a Copper Interlayer

Résumé

Sheets of aluminum 7075 and titanium Ti-6Al-4V alloys were successfully joined using the spark plasma sintering (SPS) process. A copper foil was placed as an interlayer between the two surfaces. The bonding was made at 480 °C, 500 °C, and 520 °C with a holding time of 10 min and under a uniaxial pressure of 5 MPa and 10 MPa. The obtained bonds were analyzed by scanning electron microscopy, energy dispersive spectroscopy (SEM/EDS), and wavelength dispersive spectroscopy (WDS). It was found that copper diffused away through Al7075 and formed Al2Cu intermetallics but was not present at the joint region. The investigation of the fractured surfaces using X-ray diffraction (XRD) showed that the joint region contained TiAl3, TiAl2, and Ti3Al intermetallic compounds. The presence of the Cu foil was believed to hinder the formation of Al3Ti observed in previous studies by allowing more Ti to diffuse into the Al side.
Fichier principal
Vignette du fichier
Alhazaa 2022.pdf (2.66 Mo) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte

Dates et versions

hal-03800153 , version 1 (06-10-2022)

Identifiants

Citer

Abdulaziz Alhazaa, Hamad Albrithen, Mahmoud Hezam, Muhammad Ali Shar, Ibrahim Alhwaimel, et al.. Diffusion Bonding of Al7075 to Ti-6Al-4V by Spark Plasma Sintering and Using a Copper Interlayer. Crystals, 2022, 12 (9), pp.1293. ⟨10.3390/cryst12091293⟩. ⟨hal-03800153⟩
52 Consultations
27 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More