Nanocrystalline BaCo 3 (VO 4 ) 2 (OH) 2 with a kagome lattice of Co( ii ) ions: synthesis, crystal structure and magnetic properties - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Journal of Materials Chemistry C Année : 2022

Nanocrystalline BaCo 3 (VO 4 ) 2 (OH) 2 with a kagome lattice of Co( ii ) ions: synthesis, crystal structure and magnetic properties

Résumé

We report an initial magnetic study of highly crystalline nanoparticles of the layered-kagome compound BaCo3(VO4)(2)(OH)(2). Quasi-spherical nanoparticles with size in the range of 9-25 nm were elaborated for the first time via a new synthetic route at ambient pressure. Rietveld refinement of X-ray diffraction data, vibrational spectroscopies and high-resolution scanning transmission electron microscopy indicates that the rhombohedral crystal structure of BaCo3(VO4)(2)(OH)(2) is not modified by nanostructuring. Magnetisation measurements are consistent with high-spin Co2+ ions for which unquenched orbital angular momentum is present. Temperature-dependent magnetic susceptibility shows no apparent magnetic ordering or spin freezing down to 2 K and suggests finite-size or surface effects at low temperatures.
Fichier principal
Vignette du fichier
Vesigneite-Co_NPs-1.pdf (404.56 Ko) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03595583 , version 1 (12-07-2022)

Identifiants

Citer

R. Dessapt, L. Lajaunie, J. Calvino, P. Deniard, I. Trenque, et al.. Nanocrystalline BaCo 3 (VO 4 ) 2 (OH) 2 with a kagome lattice of Co( ii ) ions: synthesis, crystal structure and magnetic properties. Journal of Materials Chemistry C, 2022, 10 (9), pp.3287-3291. ⟨10.1039/d1tc04372b⟩. ⟨hal-03595583⟩
36 Consultations
49 Téléchargements

Altmetric

Partager

Gmail Mastodon Facebook X LinkedIn More