Preparation and characterisation of green nano-sized ceramic pigments with the spinel structure AB2O4 (A = Co, Ni and B = Cr, Al) - Archive ouverte HAL Access content directly
Journal Articles Solid State Communications Year : 2021

Preparation and characterisation of green nano-sized ceramic pigments with the spinel structure AB2O4 (A = Co, Ni and B = Cr, Al)

Abstract

Inorganic pigments based on AB2O4 (A = Co, Ni; B = Cr, Al) spinel structures with green colour were successfully synthesised by the polymeric route. The effect of the substitution of trivalent and divalent cations on the structural, optical and morphological properties of the pigments was investigated. The synthesised nanopowders were examined using thermogravimetry-differential thermal analysis (TG-DTA), X-ray diffraction (XRD), scanning electron microscopy (SEM), Brunauer–Emmett–Teller analysis (BET), UV–vis diffuse reflectance measurements, and CIEL*a*b* colorimetric analyses. The results show that the CoCr2O4 spinel and the spinels substituted by nickel and aluminium cations were obtained with a single phase after heat treatment at 900 °C. The produced powders present shades of the green colour with improvement in morphology for the substituted samples. The Ni0·5Co0·5CrAlO4 nanoparticles consisted of grains of quasi-spherical shape with sizes between 50 and 75 nm. This powder was used in small quantities with glazes for colouring tests on the surfaces of ceramic substrates.
Fichier principal
Vignette du fichier
106-pre proof_EL JABBAR_Preparation and characterisation_Sol State Com.pdf (1.68 Mo) Télécharger le fichier
Origin : Files produced by the author(s)

Dates and versions

hal-03402312 , version 1 (25-10-2021)

Identifiers

Cite

Youssef El Jabbar, Hind Lakhlifi, Rachida El Ouatib, Lahcen Er-Rakho, Sophie Guillemet-Fritsch, et al.. Preparation and characterisation of green nano-sized ceramic pigments with the spinel structure AB2O4 (A = Co, Ni and B = Cr, Al). Solid State Communications, 2021, 334-335, pp.114394. ⟨10.1016/j.ssc.2021.114394⟩. ⟨hal-03402312⟩
36 View
37 Download

Altmetric

Share

Gmail Facebook Twitter LinkedIn More