Article Dans Une Revue Journal of Magnetism and Magnetic Materials Année : 2020

Loss decomposition in plastically deformed and partially annealed steel sheets

Résumé

There is an increasing interest in the optimization of non-oriented electrical steels for applications under excitation frequencies above 400 Hz. This paper discusses the possibility of a new manufacturing procedure where skin-pass and subsequent heat treatment for recovery are applied as the two last stages of sheet processing. Samples from a commercial non-oriented 3% silicon steel were submitted to a 2.5% thickness reduction and heat treated at temperatures ranging between 600 and 850 °C for 2 hours. It is shown that, although the hysteresis loss increases with plastic deformation, the excess loss decreases in such a way that under increasing magnetizing frequencies the total energy loss of the deformed and recovered sample becomes lower than in the starting material. The higher the annealing temperature the lower the frequency at which crossover of the loss curves occur, as long as full recrystallization does not occur. It is assumed that with the dislocation structures left in the deformed and partially recovered samples one achieves a condition of increased fragmentation of the magnetization process, that is, increased number of concurring correlation regions (Magnetic Objects). The corresponding decrease of the excess loss component can eventually overcompensate for the deterioration of the quasi-static magnetic properties and lead to lower total losses. .
Fichier principal
Vignette du fichier
article.pdf (997.28 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-03000534 , version 1 (12-11-2020)

Identifiants

Citer

F.J.G. Landgraf, C. Ragusa, D. Luiz Rodrigues, M Botani de Souza Dias, Olivier de La Barrière, et al.. Loss decomposition in plastically deformed and partially annealed steel sheets. Journal of Magnetism and Magnetic Materials, 2020, 502, pp.166452. ⟨10.1016/j.jmmm.2020.166452⟩. ⟨hal-03000534⟩
109 Consultations
90 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More