Co-sputtered Pr 3+ -doped Ga-Ge-Sb-Se active waveguides for mid-infrared operation

Yannick Ledemi
  • Fonction : Auteur
  • PersonId : 861890

Résumé

This work reports on the properties of luminescent waveguides based on quaternary GaGe -Sb-Se amorphous thin films doped with praseodymium. The waveguides were fabricated via magnetron co-sputtering followed by inductively coupled plasma reactive ion etching. The initial thin films thickness and optical properties were assessed and the spectroscopic properties of the waveguides were measured. The measurements show promising results-it is possible to obtain midinfrared fluorescence at 2.5 and 4.5 µm by injecting near infrared light at 1.5 µm as the pump beam. By comparing waveguides with various praseodymium concentrations, the optimal doping content for maximum fluorescence intensity was identified to be close to 4100 ppmw. Finally, correlation between the intensity of mid-infrared emission and the width/length of the waveguide is shown.
Fichier principal
Vignette du fichier
Pr-Selenide wgs Opt Exp-HA.pdf (1.11 Mo) Télécharger le fichier

Dates et versions

hal-02957437 , version 1 (01-04-2021)

Identifiants

Citer

Geoffrey Louvet, Simone Normani, Loïc Bodiou, Jan Gutwirth, Jonathan Lemaitre, et al.. Co-sputtered Pr 3+ -doped Ga-Ge-Sb-Se active waveguides for mid-infrared operation. Optics Express, 2020, 28 (15), pp.22511. ⟨10.1364/oe.398434⟩. ⟨hal-02957437⟩
71 Consultations
72 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More