Influence of gas atmosphere (Ar or He) on the laser powder bed fusion of a Ni-based alloy - Archive ouverte HAL Access content directly
Journal Articles Journal of Materials Processing Technology Year : 2021

Influence of gas atmosphere (Ar or He) on the laser powder bed fusion of a Ni-based alloy

Abstract

The gaseous atmosphere plays a major role in the quality of the manufactured parts in Laser Powder Bed Fusion (L-PBF) by protecting the metal from high temperature oxidation. If argon and nitrogen are the most commonly used gases, helium has almost never been considered as a possible candidate as a chemically inert shielding gas. To provide a better understanding of the influence of the gas atmosphere on the process stability, a comparative study of L-PBF manufacturing under argon and helium atmospheres has been carried out, considering a nickel-based alloy Inconel® 625 and a single bead configuration. To this end, in-situ process measurements were carried out on a dedicated experimental setup. The melt pool behaviour, the expansion of the vapour plume and the amount of spatters were evaluated with high-speed imaging for the two gases considered, together with the final L-PBF bead dimensions. Results were also compared to single fusion beads carried out in an industrial L-PBF machine for a comparable range of volume energy densities. The influence of the shielding atmosphere on L-PBF single beads was as follows: (1) dimensions of beads were shown to be constant whatever the gas; (2) fewer and smaller spatters were produced under helium atmosphere, especially for high volume energy densities. Physical mechanisms were then discussed to understand those specific effects.
Fichier principal
Vignette du fichier
PIMM_ JMPT_2020_TRAORE.pdf (20.8 Mo) Télécharger le fichier
Origin Files produced by the author(s)
Loading...

Dates and versions

hal-02937706 , version 1 (14-09-2020)

Identifiers

Cite

Socona Traore, Matthieu Schneider, Imade Koutiri, Frédéric Coste, Rémy Fabbro, et al.. Influence of gas atmosphere (Ar or He) on the laser powder bed fusion of a Ni-based alloy. Journal of Materials Processing Technology, 2021, 288, pp.1-18. ⟨10.1016/j.jmatprotec.2020.116851⟩. ⟨hal-02937706⟩
215 View
73 Download

Altmetric

Share

Gmail Mastodon Facebook X LinkedIn More