Structural modifications induced by ion irradiation and temperature in boron carbide B$_4$C
Résumé
Already used as neutron absorber in the current French nuclear reactors, boron carbide (B$_4$C) is also considered in the future Sodium Fast Reactors of the next generation (Gen IV). Due to severe irradiation conditions occurring in these reactors, it is of primary importance that this material presents a high structural resistance under irradiation, both in the ballistic and electronic damage regimes. Previous works have shown an important structural resistance of boron carbide even at high neutron fluences. Nevertheless, the structural modification mechanisms due to irradiation are not well understood. Therefore the aim of this paper is to study structural modifications induced in B$_4$C samples in different damage regimes.