Novel calcium phosphate/PCL graded samples: Design and development in view of biomedical applications

Résumé

Scaffolds for bone tissue engineering require a combination of bioactivity and bioresorption at the sample surface and high mechanical properties in the bulk. This work presents a novel calcium phosphate (CaP)/ polycaprolactone (PCL) scaffold with graded composition and porosity fraction. The scaffold is made of (i) a dense hydroxyapatite (HA)/β-tricalcium phosphate (β-TCP) core, (ii) a macroporous HA/β-TCP transition layer and (iii) a macroporous PCL/(HA/β-TCP) external layer. The ceramic layers were fabricated by gel-casting whereas the outer composite layer was obtained by a solvent casting/particle leaching process. The microstructure, phase composition and biodegradation of the scaffolds were characterized. The gradient of porosity was clearly obtained whereas the gradation of phase composition was less pronounced. An in vitro dissolution test was performed by immersing the scaffolds in a TRIS solution. The results showed a dissolution phenomenon with possible differentiated mechanisms in the different layers, in relation with the targeted multi-functionality.

Domaines

Matériaux
Fichier principal
Vignette du fichier
2019_Publi_MSEC_version_auteur.pdf (2.63 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-02475326 , version 1 (08-02-2021)

Identifiants

Citer

Clémence Petit, Jean-Marc Tulliani, Solene Tadier, Sylvain Meille, Jérome Chevalier, et al.. Novel calcium phosphate/PCL graded samples: Design and development in view of biomedical applications. Materials Science and Engineering: C, 2019, 97, pp.336-346. ⟨10.1016/j.msec.2018.12.044⟩. ⟨hal-02475326⟩
68 Consultations
150 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More