Influence of Water Vapour on the Rate of Oxidation of a Ni–25wt.%Cr Alloy at High Temperature

Patrice Berthod
Lionel Aranda
Stéphane Mathieu
Michel Vilasi

Résumé

The effect of water vapor on the oxidation behavior of a Ni-25wt.%Cr alloy in air was studied between 1000 and 1300°C by comparing, after test in dry air and in a humidified air, mass gain results and surface / sub-surface metallographic observations. It is found that, in the conditions of the present study, the transient oxidation at the beginning of the isothermal stage and the isothermal oxidation are both slightly slower in wet air than in dry air. The oxide formed in wet air over the surface tends to be less coarse and less thick than the one formed in dry air. The chromium depletion depths in the sub-surface are similar between the two atmospheres but the concentration at the oxide / alloy interface is higher for wet air than for dry air oxidation. The oxide scale formed in wet air seems more resistant against spallation at cooling than the scale formed in dry air.
Fichier principal
Vignette du fichier
OxidationOfMetals2013p517.pdf (444.86 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02189092 , version 1 (19-07-2019)

Identifiants

Citer

Patrice Berthod, Lionel Aranda, Stéphane Mathieu, Michel Vilasi. Influence of Water Vapour on the Rate of Oxidation of a Ni–25wt.%Cr Alloy at High Temperature. Oxidation of Metals, 2013, 79 (5-6), pp.517-527. ⟨10.1007/s11085-012-9339-x⟩. ⟨hal-02189092⟩
78 Consultations
348 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More