Journal Articles Dental Materials Year : 2016

Effect of loading configuration on strength values in a highly transformable zirconia‐based composite

Abstract

Objectives: The aim of this work was to determine mechanical properties of a highly transformable 10Ce-TZP/Al2O3/La2AlO3 composite, currently developed as a biomaterial for dental application, and to investigate the effect of loading configuration on its flexural strength. Methods: Fracture toughness is determined by the single-edge-V-notched beam (SEVNB) method. Strength measurements were conducted by four-point bending and biaxial bending tests (piston-on-three balls) according to ISO 6872, dedicated to ceramic materials in dentistry. Results: Strength obtained by either four-point or biaxial bending are very different, and take the values of 596MPa and 1470MPa respectively. It is demonstrated that the difference in measured strength cannot be attributed to the effect of volume on strength, generally predicted by the standard Weibull analysis, but to different transformation behaviors for the two bending configurations. More extensive transformation occurs in the biaxial configuration, with a lower autocatalytic transformation stress threshold, resulting to substantial compressive residual stresses. Significance: The significant influence of the loading configuration on the strength should be integrated when designing a component from a highly transformable ceramic.
Fichier principal
Vignette du fichier
Touaiher2016.pdf (352.77 Ko) Télécharger le fichier
Origin : Files produced by the author(s)

Dates and versions

hal-01670817 , version 1 (21-01-2022)

Licence

Attribution - NonCommercial

Identifiers

Cite

Imane Touaiher, Malika Saadaoui, Jérome Chevalier, Helen Reveron. Effect of loading configuration on strength values in a highly transformable zirconia‐based composite. Dental Materials, 2016, 32 (9), pp.e211-e219. ⟨10.1016/j.dental.2016.06.023⟩. ⟨hal-01670817⟩
55 View
125 Download

Altmetric

Share

Gmail Facebook X LinkedIn More