Measurement of Strain Localization Resulting from Monotonic and Cyclic Loading at 650°C in Nickel Base Superalloys

Résumé

A methodology is presented for the use of the oxide scale that develops in polycrystalline Ni-base super-alloys at service temperature, as a speckle pattern for μm-scale resolution strain measurements. Quantitative assessment of the heterogeneous strain field at the grain scale is performed by high-resolution SEM digital image correlation under monotonic and cyclic loading in polycrystalline Ni-base superalloys up to 650 • C. In the René 88DT superalloy, strain localization is observed near twin boundaries during low cycle fatigue (LCF) at intermediate temperatures, correlating with activation of {111}}110 and {111}}112 slip systems. A strong correlation between the microstruc-tural configuration that promotes strain localization during monotonic loading and crack initiation at 650 • C in low cycle fatigue was observed.
Fichier principal
Vignette du fichier
Measurement of Strain Localization Resulting.pdf (14.67 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01662651 , version 1 (13-12-2017)

Identifiants

Citer

Jean-Charles Stinville, Mclean P. Echlin, Patrick G. Callahan, Victoria M. Miller, Damien Texier, et al.. Measurement of Strain Localization Resulting from Monotonic and Cyclic Loading at 650°C in Nickel Base Superalloys. Experimental Mechanics, 2017, 57 (8), pp.1289-1309. ⟨10.1007/s11340-017-0286-y⟩. ⟨hal-01662651⟩
77 Consultations
88 Téléchargements

Altmetric

Partager

Gmail Mastodon Facebook X LinkedIn More