Shape-memory bionanocomposites based on chitin nanocrystals and thermoplastic polyurethane with a highly crystalline soft segment
Résumé
Shape-memory bionanocomposites based on a naturally sourced segmented thermoplastic polyurethane and chitin nanocrystals were synthesized, and their mechanical properties and thermally activated shape-memory behavior were studied. The chitin nanocrystals were incorporated during the synthesis of the prepolymer made from a castor oil-based difunctional polyol and hexamethylene diisocyanate. The polymerization was completed by addition of propanediol, as a corn-sugar based chain extender, bringing the weight content of components from renewable resources to >60%. Thermal analysis of the bionanocomposites revealed a phase-separated morphology, which is composed of soft and hard domains, which bestow the material with two melting transitions at 60 and 125 C, that are exploitable for a shape memory effect. The soft segment is responsible for temporary shape fixing, while the hard segment crystallites are responsible for the permanent shape. The introduction of small amounts (0.25-2 wt %) of chitin nanocrystals was found to increase the crystallinity of the hard segment by way of nucleation, which in turn improves the shape recovery considerably. The thermally activated shape-memory behavior of the synthesized bionancomposites is exploitable with a programming and release temperature of 60 C. The materials display good in vitro cell response, as shown by short-term cytotoxicity assays, and therefore, the bionanocomposites appear to be potentially useful for biomedical applications. © 2013 American Chemical Society.