Effets thermique et mécanique de l'incorporation de déchets de mousse de polyuréthane dans un mortier
Résumé
This article presents the results of an experimental study on the use of polyurethane foam waste for the manufacture of insulating mortars. Five mortars containing various foam proportions (0%, 51%, 54%, 61% and 69% of the mortar volume) were prepared and the determination of thermal and mechanical properties, shrinkage and mass loss per desiccation made it possible to measure the influence of the foam incorporation. The thermal conductivity of the mortars with polyurethane foam is a half to a third as high as that of the reference mortar (without foam) while compressive strength decreases in a ratio from 2 to 6 according to the foam proportion. In addition, the presence of polyurethane foam in the mortars results in an important increase in shrinkage and in mass loss per desiccation.
Cet article présente les résultats d'une étude expérimentale sur l'utilisation de déchets de mousse de polyuréthanne pour la fabrication de mortiers isolants. Cinq mortiers contenant différents dosages de mousse (0%, 51%, 54%, 61% et 69% du volume de mortier) ont été préparés et la détermination de leurs propriétés thermiques et mécaniques, de leur retrait et de leur perte de masse par dessiccation a permis de mesurer l'influence de l'incorporation des déchets de mousse. La conductivité thermique des mortiers avec mousse de polyuréthanne est 2 à 3 fois inférieure à celle du mortier référence (sans mousse) tandis que la résistance en compression diminue dans un rapport de 2 à 6 selon le dosage en mousse utilisé. Par ailleurs, la présence de mousse de polyuréthanne dans les mortiers se traduit par une augmentation importante du retrait et de la perte de masse par dessiccation. Ces résultats s'expliquent par la forte porosité et la faible résistance mécanique du polyuréthanne alvéolaire.
| Origine | Fichiers produits par l'(les) auteur(s) |
|---|