Sub-boundary mobilities during recovery of binary Al-Mn alloys

Fabrice Barou
Claire Maurice
Jean-Marie Feppon
  • Fonction : Auteur
Julian Driver
  • Fonction : Auteur

Résumé

Two, high purity, Al-0.1 and 0.3wt%Mn alloys have been cold deformed in plane strain compression to strains of order 1.8 and the kinetics of subsequent recovery by sub-grain coarsening during annealing at 150-300°C measured by high resolution FEG-SEM EBSD. Accurate sub-grain size and misorientation distributions and their evolution with time and temperature have been determined. The average growth rates are then used to estimate the sub-grain boundary mobilities. Growth is analyzed by two well-known growth laws for the average sub-grain size δ (t): i) the standard relation for grain growth: where the exponent n takes values of 2-8 and ii) the relation proposed by Nes for dislocation climb in sub-grain walls: It is shown that the latter relation gives a better fit with the data in terms of the time and temperature dependence of the sub-grain sizes. In particular the activation energies for the logarithmic law are much closer to the values expected for solute-controlled movement of sub-boundaries.

Domaines

Matériaux
Fichier non déposé

Dates et versions

hal-00795441 , version 1 (28-02-2013)

Identifiants

Citer

Fabrice Barou, Claire Maurice, Jean-Marie Feppon, Julian Driver. Sub-boundary mobilities during recovery of binary Al-Mn alloys. Materials Science Forum, 2012, 715-716, pp.725-731. ⟨10.4028/www.scientific.net/MSF.715-716.725⟩. ⟨hal-00795441⟩
93 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Mastodon Facebook X LinkedIn More