Stabilization of cubic structure in Mn-doped hafnia

Résumé

The compounds Hf1- xMnxO2- d (x = 0-0.5) have been synthesized by conventional solid state reaction method in Ar. Rietveld analysis of X-ray diffraction data has shown that the Mn-doped HfO2 undergoes a structural transformation from monoclinic to cubic phases, which is significantly dependent on the Mn content under current synthesis conditions. The stabilized cubic structure by multivalent Mn ion doping can transform to the monoclinic structure when annealed at high temperature in air. Transmission electron microscopy and electron diffraction investigations have also confirmed the existence of the high-temperature cubic structure. A mechanism of stabilizing the high-temperature cubic phase in the Hf1- xMnxO2- d system has been analyzed based on considerations of manganese substitution effect for hafnium ions and oxygen vacancy formation.

Domaines

Matériaux
Fichier principal
Vignette du fichier
355-Publi_Gao_manuscript_Manganese_Doped_Hafnia.pdf (2.17 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-00714963 , version 1 (06-07-2012)

Identifiants

Citer

Ling Gao, Lian Zhou, Jianqing Feng, Lifeng Bai, Zhongyuan Liu, et al.. Stabilization of cubic structure in Mn-doped hafnia. Ceramics International, 2012, 38, pp.2305-2311. ⟨10.1016/j.ceramint.2011.10.082⟩. ⟨hal-00714963⟩

Collections

UGA CNRS NEEL
164 Consultations
467 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More