PbZr0.52Ti0.48O3 and SrBi2Nb2O9 ferroelectric oxides integrated with YBa2Cu3O7 superconductor in multilayers epitaxially grown by pulsed laser deposition - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Journal de Physique IV Proceedings Année : 2001

PbZr0.52Ti0.48O3 and SrBi2Nb2O9 ferroelectric oxides integrated with YBa2Cu3O7 superconductor in multilayers epitaxially grown by pulsed laser deposition

Résumé

Multilayers of PbZr0.52Ti0.48O3 (PZT) or SrBi2Nb2O9 (SBN) ferroelectrics (F) and YBa2Cu3O7 (YBaCuO) superconductor (S) have been grown by pulsed laser deposition. F/S or S/F bilayers as well as S/F/S trilayers deposited on SrTiO3 and MgO were epitaxially grown, as evidenced by x-ray diffraction (XRD) inθ -2θ and φ-scans modes, reflection high energy electron diffraction (RHEED) or electron channeling patterns (ECP). Superconducting YBaCuO films deposited on PZT exhibit a critical temperature, Tc, of about 86 K slightly below the value routinely obtained in the same deposition conditions on bare (100)SrTiO3 substrate (typically 88-89 K). By contrast, the Tc of YBaCuO films on SBN, either on (100)SrTiO3 or on (100)MgO is close to 88-89 K suggesting that SBN can be a good candidate as ferroelectric buffer layer for the growth of YBaCuO, especially on MgO for which a graphoepitaxial mechanism tends to limit the YBaCuO growth quality. In the case of F/S layers, hysteresis loops of PZT on YBaCuO show a saturated polarization larger than 30 µC/cm2 and a coercive field of about 70 kV/cm. Secondary ion mass spectrometry (SIMS) experiments have been performed in order to correlate interdiffusion mechanisms with both structural data and physical properties.

Domaines

Matériaux
Fichier principal
Vignette du fichier
Duclere2001.pdf (435.67 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-00152480 , version 1 (23-08-2022)

Licence

Paternité - Pas d'utilisation commerciale

Identifiants

Citer

Jean-René Duclere, Maryline Guilloux-Viry, A. Perrin, Caroline Soyer, Eric Cattan, et al.. PbZr0.52Ti0.48O3 and SrBi2Nb2O9 ferroelectric oxides integrated with YBa2Cu3O7 superconductor in multilayers epitaxially grown by pulsed laser deposition. Journal de Physique IV Proceedings, 2001, International Conference on Thin Film Deposition of Oxide Multilayers Hybrid Structures, 11 (PR11), pp.29-33. ⟨10.1051/jp4:20011104⟩. ⟨hal-00152480⟩
175 Consultations
16 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More