Thermal evolution of deuterium in 4H-SiC

Résumé

4H-SiC samples were implanted at room temperature with 30 keV D + ions at a dose of 5x10 16 D + /cm². Nuclear reaction analysis (NRA) and secondary ion mass spectroscopy (SIMS) measurements were performed to study the deuterium profiles after subsequent annealing at 1000-1250°C for 10min.Also, analytical techniques: RBS/C and thermal desorption spectroscopy (TDS) were carried out to characterize the evolution of implantation induced defects upon annealing. According to the NRA measurements, no deuterium release was found in the sample annealed at 1000°C. However, increasing the temperature to 1150°C led to a 40% decrease of deuterium content. Similar results about the evolution of D profiles upon annealing have also been obtained by SIMS measurements. In addition, SIMS measurements show that the maximum of the deuterium concentration shifts to the surface. Deuterium desorption at annealing temperatures higher than 1000°C was further confirmed by TDS experiments. Results from RBS/C indicated that during the desorption of deuterium, the implantation induced damage was annealed. These results are discussed.
Fichier principal
Vignette du fichier
PAPER.pdf (196.78 Ko) Télécharger le fichier

Dates et versions

hal-00003911 , version 1 (15-01-2005)

Identifiants

  • HAL Id : hal-00003911 , version 1

Citer

Romain Delamare, E. Ntsoenzok, T. Sauvage, A. Shiryaev, A. van Veen, et al.. Thermal evolution of deuterium in 4H-SiC. 2002, pp.269. ⟨hal-00003911⟩
60 Consultations
93 Téléchargements

Partager

Gmail Facebook X LinkedIn More