Corrosion of ceramic matrix composites

T. Scanu
  • Fonction : Auteur
Ph. Colomban

Résumé

Air stable ceramic matrix composites are promising for thermostructural applications such as aircraft engine parts. Turbine parts are subject to both sulphuric acid and sodium molten salts corrosion due to sulphate traces in engine fuel and to the NaCl air content. The chemical stability is a very important criterion but this point has not received much attention to date. We report here a study of acidic and sodium corrosion of various aluminosilicate matrices : LAS matrices (Li2OAl2O32-6SiO2, nP2O5) in the amorphous, β eucryptite and β spodumene forms, BAS matrix (BaOAl2O32SiO2) in the form of monoclinic and hexagonal celsian, NASICON matrix (Na3Zr2Si2PO12) and mullite matrix. Microstructure damages and ion exchange have been analysed by X-ray diffraction, IR absorption, scanning electron microscopy and Raman microprobe. Drastic corrosion is observed for β spodumene containing composites with the formation of strong hydrogen bond or with the cell expansion due to Li/NA+ exchange. Medium acidic attack occurs for glassy LAS, β eucryptite, BAS and NASICON matrix composites. On the other hand, β eucryptite, NASICON and monoclinic celsian resist to alkaline melts. Mullite matrix composites are never corroded.

Domaines

Articles anciens
Fichier principal
Vignette du fichier
ajp-jp4199303C7308.pdf (1.72 Mo) Télécharger le fichier
Origine : Accord explicite pour ce dépôt
Loading...

Dates et versions

jpa-00251952 , version 1 (04-02-2008)

Identifiants

Citer

T. Scanu, Ph. Colomban. Corrosion of ceramic matrix composites. Journal de Physique IV Proceedings, 1993, 03 (C7), pp.C7-1927-C7-1930. ⟨10.1051/jp4:19937308⟩. ⟨jpa-00251952⟩

Collections

LIAMA AJP
54 Consultations
183 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More