Processing of submicron a-alumina powders doped with Mg-physical and chemical characterization

M. Filal
  • Fonction : Auteur
D. Monceau
G. Petot-Ervas
  • Fonction : Auteur
C. Petot
  • Fonction : Auteur
J. Zao
  • Fonction : Auteur

Résumé

This work examines the influence of the thermal treatment conditions at T > 1150°C, on the microstructure and microchemistry of submicron a-alumina powders doped with '500 and 1650 ppm by weight of MgO. The powders have been characterized by XPS, TEM, SEM, BET surface area measurements and chemical analysis. Quantitative XPS analysis show a strong segregation of Mg at the near surface of the grains. The determining factor is the size of the grains and it has been possible to relate the amount of Mg at the periphery of the grains to the BET surface area measurements.

Domaines

Articles anciens
Fichier principal
Vignette du fichier
ajp-jp4199303C7227.pdf (115.81 Ko) Télécharger le fichier
Origine : Accord explicite pour ce dépôt

Dates et versions

jpa-00251863 , version 1 (04-02-2008)

Identifiants

Citer

M. Filal, D. Monceau, G. Petot-Ervas, C. Petot, J. Zao. Processing of submicron a-alumina powders doped with Mg-physical and chemical characterization. Journal de Physique IV Proceedings, 1993, 03 (C7), pp.C7-1459-C7-1462. ⟨10.1051/jp4:19937227⟩. ⟨jpa-00251863⟩

Collections

AJP
30 Consultations
149 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More