High temperature behaviour and oxidation resistance of carbon-boron-nitrogen compounds obtained by LPCVD

A. Derre
  • Fonction : Auteur
  • PersonId : 1056910
  • IdRef : 033675163
L. Filipozzi
  • Fonction : Auteur
F. Peron
  • Fonction : Auteur

Résumé

Coatings of carbon-boron-nitrogen compounds with various compositions are obtained in a low pressure chemical vapour deposition process using acetylene, boron trichloride, ammonia and hydrogen as input gases. Compositions are located in the ternary system C-BN-"BC3". The structure of the films is a graphitic turbostratic one for the whole composition range but carbonrich deposits exhibit greater coherence length Lc than boron nitride-rich ones. The high temperature behaviour is studied for three specific compositions : C0.82B0.14N0.04, C0.50B0.31N0.19 and C0.78B0.22. In an inert atmosphere no mass loss is observed up to 2250°C while graphitization and formation of boron carbide occur. Based on electron probe micro analysis, depletion of boron and nitrogen happens only in the few micrometers near the surface of the sample. Above 2500°C, B13C2 evaporates and a graphite-like material is formed. In a dry air atmosphere, oxidation occurs above 800°C with a slow kinetics. A boron oxide layer protects the sample up to 1000°C. Above this temperature, volatilization of B2O3 occurs and oxidation is greatly enhanced. Of special interest seems to be the C0.78B0.22 coating which exhibits the lowest oxidation rate. Such deposits could then present a way to protect carbon-carbon composites at moderate temperature in the form of an external coating or better of an intermediate layer between fibres and matrix.

Domaines

Articles anciens
Fichier principal
Vignette du fichier
ajp-jp4199303C325.pdf (419.81 Ko) Télécharger le fichier
Origine Accord explicite pour ce dépôt

Dates et versions

jpa-00251382 , version 1 (04-02-2008)

Identifiants

Citer

A. Derre, L. Filipozzi, F. Peron. High temperature behaviour and oxidation resistance of carbon-boron-nitrogen compounds obtained by LPCVD. Journal de Physique IV Proceedings, 1993, 03 (C3), pp.C3-195-C3-202. ⟨10.1051/jp4:1993325⟩. ⟨jpa-00251382⟩

Collections

AJP
33 Consultations
610 Téléchargements

Altmetric

Partager

Gmail Mastodon Facebook X LinkedIn More