Article Dans Une Revue Colloids and Surfaces A: Physicochemical and Engineering Aspects Année : 2023

Unification of rheology of thixotropic yield stress fluids and screen printing properties of pastes

Jinbo Bai
Shenghua Ma
  • Fonction : Auteur
  • PersonId : 1604640
Hui Wang
  • Fonction : Auteur
  • PersonId : 848036

Résumé

At present, the electrode width of solar cells has been successfully reduced to less than 20 µm. Ensuring its morphology and aspect ratio remains a major challenge to further reducing the electrode width, which puts higher requirements on the performance of the paste. Previous studies have focused less on selecting organic carrier components and the relationship between carrier and paste printing suitability. Therefore, in this study, considering the wettability of the solvent to the silicon wafer, the solubility to the binder and the boiling point, the selection method of the mixed solvent for the organic carrier was given. The Herschel-Buckley model was introduced to characterize the ffow behavior of the organic carrier. Furthermore, the model parameters were uniffed with the printability of the paste and the organic carrier model parameters corresponding to the paste with good printability were contributed. The results showed that when the consistency index (K) was 21.883 and the exponent (n) was 0.1545, the aspect ratio of the electrode was the largest. When the yield stress (5.38 Pa) and thixotropic loop area (707.71 Pa s − 1 ) were the largest, the morphology of the electrode was the most regular.

Domaines

Fichier principal
Vignette du fichier
Unification of rheology of thixotropic yield stress fluids and screen printing properties of pastes.pdf (2.32 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)
Licence

Dates et versions

hal-05351242 , version 1 (06-11-2025)

Licence

Identifiants

Citer

Chaobin Mao, Yuxin Tian, Xingyu Zhou, Jinbo Bai, Shenghua Ma, et al.. Unification of rheology of thixotropic yield stress fluids and screen printing properties of pastes. Colloids and Surfaces A: Physicochemical and Engineering Aspects, 2023, 682, pp.132982. ⟨10.1016/j.colsurfa.2023.132982⟩. ⟨hal-05351242⟩
38 Consultations
195 Téléchargements

Altmetric

Partager

  • More