Co-Effect of pH Control Agent and pH Value on the Physical Properties of ZnO Thin Films Obtained by Chemical Bath Deposition for Potential Application in Dye-Sensitized Solar Cells

Ayayi Claude Ahyi
  • Fonction : Auteur
  • PersonId : 1594952
Muthiah Haris
  • Fonction : Auteur
  • PersonId : 1594953
Muthusamy Senthilkumar
Bruno Grandidier

Résumé

This study presents the influence of pH control agents and pH value on the physical properties of ZnO thin films obtained by chemical bath deposition. ZnO thin films were synthesized on glass substrates using precursor solutions of different pHs prepared from two bases: sodium hydroxide (NaOH) and ammonia (NH3). The effect of pH values on the morphological, structural, and optical properties of ZnO thin films was investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), and UV-Visible spectroscopy. XRD results showed that all the synthesized ZnO thin films are polycrystalline and crystallize in a hexagonal wurtzite structure. The crystallite size, calculated using the Debye-Scherrer formula, varied from 10.50 nm to 11.69 nm for ZnO thin films obtained with NH3 and from 20.79 nm to 27.76 nm for those obtained with NaOH. FTIR analysis confirmed the presence of functional groups. SEM images indicated that not only the base but also the pH affects the morphology of the films, giving rise to different granular shapes. Overall, the ZnO thin films obtained with NaOH looked more mesoporous compared to those obtained with NH3. Optical characterization results showed that whatever the base used, the pH of the precursor solution affected the ZnO thin film transmittance. Films synthesized with NH 3 exhibited the best transmittance (80%) at pH 8.5, while the best transmittance (81%) of films synthesized with NaOH was obtained at pH 8 in the visible region. Based on optical and morphological properties, ZnO films obtained from NH3 at pH 8.5 are found to be more suitable as photoanodes in dye-sensitized solar cells.

Fichier principal
Vignette du fichier
surfaces-08-00046.pdf (2.62 Mo) Télécharger le fichier
Origine Fichiers éditeurs autorisés sur une archive ouverte
Licence

Dates et versions

hal-05313801 , version 1 (14-10-2025)

Licence

Identifiants

Citer

Alphonse Déssoudji Gboglo, Mazabalo Baneto, Komlan Segbéya Gadedjisso-Tossou, Ognanmi Ako, Ayayi Claude Ahyi, et al.. Co-Effect of pH Control Agent and pH Value on the Physical Properties of ZnO Thin Films Obtained by Chemical Bath Deposition for Potential Application in Dye-Sensitized Solar Cells. Surfaces, 2025, 8 (3), pp.46. ⟨10.3390/surfaces8030046⟩. ⟨hal-05313801⟩
119 Consultations
100 Téléchargements

Altmetric

Partager

  • More