Synthesis and Characterization of Polyaniline/ CoxCr0.5-xFe2O4 Nanocomposites for ElS Applications

Résumé

In situ polymerization was used to synthesize polyaniline (PANI)/CoxCr0.5-xFe2O4(x=0, 0.1, 0.3) nanocomposites with good electromagnetic shielding effectiveness. X-ray diffraction, Field emission scanning electron microscopy, and Vibrating sample magnetometer techniques were used to investigate PANI/ CoxCr0.5-xFe2O4(x=0, 0.1, 0.3) nanocomposites . Electromagnetic Interference (EMI) shielding effectiveness (SE) tests for PANI/ CoxCr0.5-xFe2O4(x=0, 0.1, 0.3) nanocomposites have also been carried out as a function of frequency at room temperature. Conduction mechanisms in PANI/ CoxCr0.5-xFe2O4(x=0, 0.1, 0.3) nanocomposites are in accordance with the electron hopping model. Furthermore, SE was shown to decrease as the applied frequency was increased in all generated samples. SE values for Polyaniline/CoxCr0.5-xFe2O4(x=0, 0.1, 0.3) nanocomposites rise with increasing Copper content in the composite in the current study.

Domaines

Fichier non déposé

Dates et versions

hal-05262570 , version 1 (16-09-2025)

Identifiants

  • HAL Id : hal-05262570 , version 1

Citer

R Madhukumar, Karabasappa H Byadgi, C. G Renuka, N. R Mohan. Synthesis and Characterization of Polyaniline/ CoxCr0.5-xFe2O4 Nanocomposites for ElS Applications. New Innovations in Chemistry and Biochemistry Vol. 5, BP International, pp.11-17, 2021. ⟨hal-05262570⟩
13 Consultations
0 Téléchargements

Partager

  • More