Oxygen Embrittlement Kinetics at 500–600 °C of the Ti–6Al–4V Alloy Fabricated by Laser and Electron Powder Bed Fusion

Résumé

Ti-6Al-4V alloys manufactured by laser or electron powder bed fusion (L-PBF and E-PBF) with or without hipping treatment have different microstructures from foundry alloys. Their oxidation kinetics at high temperatures between 500 and 600 °C for durations up to 2,000 h were compared. The effect of oxidation on their room temperature tensile embrittlement was quantified. It was shown that the growth kinetics of the brittle fracture zone, of the zone with cracks at 1% strain, and of the oxygen diffusion zone were perfectly correlated. Therefore, the embrittlement was confirmed to be due to oxygen ingress below the oxide scale and the kinetics were independent of the microstructure.

Fichier principal
Vignette du fichier
2024_HTCM Casadebaigt kinetics embrittlement.pdf (1.39 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)
Licence

Dates et versions

hal-04680518 , version 1 (18-11-2024)

Licence

Identifiants

Citer

Antoine Casadebaigt, Daniel Monceau, Jonathan Hugues. Oxygen Embrittlement Kinetics at 500–600 °C of the Ti–6Al–4V Alloy Fabricated by Laser and Electron Powder Bed Fusion. High Temperature Corrosion of Materials, 2024, 101, pp.107-122. ⟨10.1007/s11085-024-10249-8⟩. ⟨hal-04680518⟩
82 Consultations
197 Téléchargements

Altmetric

Partager

  • More