Mechanical properties of Li2MoO4 single crystals

A. Ahmine
  • Fonction : Auteur
P. Djemia
  • Fonction : Auteur
M. Fivel
  • Fonction : Auteur
D. Faurie
  • Fonction : Auteur
N. Girodon-Boulandet
  • Fonction : Auteur
M. Velazquez
L. Xuan
  • Fonction : Auteur

Résumé

Mechanical properties of lithium molybdate single crystals, Li2MoO4, are studied from room temperature to 650 °C. Density functional theory calculations gave the seven elastic constants of the rhombohedral crystal at 0 K. Brillouin light scattering experiments delivered comparable values at room temperature, and measurements up to 650 °C show a linear decrease in the constants with temperature. Nano-indentation results were typical of a brittle material with a low Young modulus and allowed deriving Young's moduli, for c (63 GPa) and m (48 GPa) faces, in agreement with those computed from measured elastic constants. Compressive rupture tests were performed. At 650 °C, the rupture stress was in the range 2–7.5 MPa. No clear evidence of a plastic regime was observed before cracking, even at temperatures close to the melting point.
Fichier non déposé

Dates et versions

hal-04602043 , version 1 (05-06-2024)

Identifiants

Citer

A. Ahmine, P. Djemia, M. Fivel, D. Faurie, N. Girodon-Boulandet, et al.. Mechanical properties of Li2MoO4 single crystals. Journal of Applied Physics, 2022, 131 (17), ⟨10.1063/5.0085260⟩. ⟨hal-04602043⟩
12 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Mastodon Facebook X LinkedIn More