Towards All-Non-Vacuum-Processed Photovoltaic Systems: A Water-Based Screen-Printed Cu(In,Ga)Se2 Photoabsorber with a 6.6% Efficiency
Résumé
During the last few decades, major advances have been made in photovoltaic systems based on Cu(In,Ga)Se2 chalcopyrite. However, the most efficient photovoltaic cells are processed under high-energy-demanding vacuum conditions. To lower the costs and facilitate high-throughput production, printing/coating processes are proving to be effective solutions. This work combined printing, coating, and chemical bath deposition processes of photoabsorber, buffer, and transparent conductive layers for the development of solution-processed photovoltaic systems. Using a sustainable approach, all inks were formulated using water and ethanol as solvents. Screen printing of the photoabsorber on fluorine-doped tin-oxide-coated glass followed by selenization, chemical bath deposition of the cadmium sulfide buffer, and final sputtering of the intrinsic zinc oxide and aluminum-doped zinc oxide top conductive layers delivered a 6.6% maximum efficiency solar cell, a record for screen-printed Cu(In,Ga)Se2 solar cells. On the other hand, the all-non-vacuum-processed device with spray-coated intrinsic zinc-oxide- and tin-doped indium oxide top conductive layers delivered a 2.2% efficiency. The given approaches represent relevant steps towards the fabrication of sustainable and efficient Cu(In,Ga)Se2 solar cells.