Evolution of the perovskite phase in UO2-based samples under conditions representative of a severe nuclear accident by XANES

Résumé

To understand the fission products behaviour during a Nuclear Severe Accident (NSA), simulated high burnup UO2 fuels produced by sintering at high temperature (SIMFUEL) were submitted to thermal treatments in conditions representative of the beginning of a Pressurized Water Reactor (PWR) severe accident. The samples made of UO2 doped with eleven fission products (FP) surrogates were thus thermally treated from 400 ​°C up to 1000 ​°C at different oxygen potentials (up to −290 ​kJ ​mol(O2)−1 at 1000 ​°C). The samples were characterized before and after the heat treatments by Secondary Electron Microscopy coupled with Energy Dispersive X-ray Spectroscopy (SEM-EDX) and X-ray Absorption Spectroscopy (XAS) at the MARS beamline, SOLEIL Synchrotron and at the FAME-UHD beamline, ESRF. Initially the SIMFUEL is constituted of a UO2 matrix, a metallic phase composed of Mo, Pd, Ru, Rh and Tc, and an oxide phase with perovskite structure depicted as (Ba, Sr)(Zr, U, RE)O3 where RE stands for Rare Earths. Around 1000 ​°C, it was found that Mo, initially contained in the metallic inclusions, oxidizes into MoO2. In the same conditions, a part of the oxidized Mo interacts with the perovskite phase containing Ba to form BaMoO4. These results will be useful to validate the theoretical models used in calculation codes and to assess thermodynamic databases, which are one of the main sources of errors when calculating a NSA sequence involving molten fuel.

Dates et versions

hal-04560311 , version 1 (26-04-2024)

Identifiants

Citer

Claire Le Gall, Vincent Klosek, Fabienne Audubert, Jacques Lechelle, Doris Drouan, et al.. Evolution of the perovskite phase in UO2-based samples under conditions representative of a severe nuclear accident by XANES. Journal of Solid State Chemistry, 2023, 319, pp.123792. ⟨10.1016/j.jssc.2022.123792⟩. ⟨hal-04560311⟩
16 Consultations
0 Téléchargements

Altmetric

Partager

More