Assembled pentasil nanosheet zeolites: Adjusting the sheet thickness through a simple and direct dual templating approach

Résumé

A simple one-step synthesis method is demonstrated, enabling the thickness of assembled silicalite nanosheets to be tuned from 2 to 30 nm. The adjustement is achieved by mixing two common organic structure-directing agents (OSDAs): tetrapropylammonium (TPA) and tetrabutylammonium (TBA). During the hydrothermal synthesis, there is a preferential uptake of TPA, and the proportion of incorporated TBA can be deduced accordingly. The proportion of TBA, known to favour silicalite nanosheets, determines the nanosheets’ thickness and the morphological variations observed

Domaines

Matériaux
Fichier principal
Vignette du fichier
Preprint_AlNahari_Alonso_2.pdf (4.22 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-04524708 , version 1 (28-03-2024)

Identifiants

Citer

Shadi Al-Nahari, Bruno Alonso. Assembled pentasil nanosheet zeolites: Adjusting the sheet thickness through a simple and direct dual templating approach. Microporous and Mesoporous Materials, 2024, 372, pp.113093. ⟨10.1016/j.micromeso.2024.113093⟩. ⟨hal-04524708⟩
1 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More