Experimental Investigation and Thermodynamic Assessment of the Cr–Ti System

Résumé

The Cr–Ti system was investigated by several experimental methods and first-principles calculations. The thermodynamic activity of the body-centered cubic solid solution was measured by Knudsen effusion mass spectrometry. The stability of all three polymorphic structures of the Laves phase (C14, C15, and C36) was determined by differential thermal analysis, and the equilibrium tie-lines with the solid solution were obtained by combining results from diffusion couples and equilibrated alloys. The enthalpy of formation of the Laves phases with the corresponding end-members were calculated using density functional theory and the obtained values were integrated in the models. The experimental and computed data available in the literature was reviewed and the binary system was assessed by the Calphad method. The present evaluation results in an improved thermodynamic description, which can describe the experimentally observed activity in a large temperature range. The temperatures of the invariant reactions between the C15 andthe C36 phase with the Cr-rich and the Ti-rich bcc solid solution were significantly modified. The difference of the temperature of transformation between the C15 and the C36 polytypes on both sides of the Laves phase is much smaller than reported previously.
Fichier non déposé

Dates et versions

hal-04501183 , version 1 (12-03-2024)

Identifiants

Citer

Agustin Flores, Sylvie Chatain, Paul Fossati, Frank Stein, Jean-Marc Joubert. Experimental Investigation and Thermodynamic Assessment of the Cr–Ti System. Journal of Phase Equilibria and Diffusion, 2024, ⟨10.1007/s11669-024-01090-2⟩. ⟨hal-04501183⟩
2 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More