High Temperature Tensile Properties and Microstructure of Ni20Cr Alloy Fabricated by Laser Powder Bed Fusion

Shubham Sanjay Joshi
Clément Keller
Williams Lefebvre

Résumé

Additive Manufacturing (AM) brings about an array of modifications in microstructure with respect to conventional routes transforming mechanical performances. These new microstructure features depend on process parameters and especially on volume energy-density delivered by the laser on powder layer. Among the different alloys manufactured by AM, Nialloys exhibit high-strength at elevated temperature opening the way of fabrication of gas turbines and jet-engine parts. Ni-superalloys experience precipitation hardening due to the formation of γ′ and γ′′ phases leading to complex microstructures. To better study the influence of the AM microstructure on Ni-alloys mechanical properties, in particular at elevated temperatures, a theoretically monophasic and binary Ni20Cr-alloy manufactured by laser powder-bed fusion was studied in this work. Remarkable Yield Strength (400 MPa) and Ultimate Tensile Strength (UTS) (600 MPa) were observed at 500°C with hardly any loss of properties from room temperature, owing to the thermal stability of cellular dendrites till 700°C. Ductility drop was reported at 700°C due to anomalous brittle behaviour of Ni-alloys. Hardening behaviour vanished at 900°C signifying the deletion of dendrites, disappearance of dislocations, diffusion of Cr from dendritic walls and growth of oxides.
Fichier sous embargo
Fichier sous embargo
0 1 1
Année Mois Jours
Avant la publication
mardi 28 mai 2024
Fichier sous embargo
mardi 28 mai 2024
Connectez-vous pour demander l'accès au fichier

Dates et versions

hal-04311476 , version 1 (28-11-2023)

Identifiants

Citer

Shubham Sanjay Joshi, Clément Keller, Williams Lefebvre, Eric Hug. High Temperature Tensile Properties and Microstructure of Ni20Cr Alloy Fabricated by Laser Powder Bed Fusion. Key Engineering Materials, 2023, 964, pp.97 - 102. ⟨10.4028/p-0wza3s⟩. ⟨hal-04311476⟩
40 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More