Surface microstructure of an IN718 3D coating manufactured by Laser Metal Deposition

Résumé

Laser Metal Deposition (LMD) is a well-known additive manufacturing (AM) process that offers the ability to repair metal parts, among other benefits. We have focused on IN718 parts that evolve in environments that strongly favor wear. Therefore, a good knowledge of the contact surface microstructure and its properties is necessary to better understand the tribological behavior of these parts. However, the microstructure of the top surface (which is most susceptible to wear) of IN718 coatings deposited by LMD is not particularly well documented in the literature. Most of the studies devoted to this alloy have focused on the study of the cross-sectional microstructure, and the few articles dealing with the top surface microstructure have been devoted to the Laser Powder Bed Fusion (LPBF) process. In this article, four IN718 coatings were successfully fabricated with high density using different scanning strategies. When viewing the microstructure from the top surface, the EBSD map showed a very heterogeneous microstructure with an alternation of fine and coarse grains. It also showed a weak overall texture, but a strong local texture within the fine and coarse grain region. EBSD analysis of the cross-sectional area of the coated section also revealed a microstructure variation along the build direction (BD) with the appearance of small grains between layers after some layers have been deposited. Analysis of both sides of the coated part allowed us to get a better understanding of the final microstructure. We were able to show that this heterogeneous microstructure leads to a spatial variation of the top surface hardness, the pattern of which is directly related to the scanning strategy. Finally, we found that the surface hardness of IN718 LMD samples is higher than that of conventionally produced IN718, which is a promising result in terms of repairing metal parts with good tribological properties.

Domaines

Matériaux
Fichier principal
Vignette du fichier
Article_microstructure_IN718_LMD-V14_After-review_compressed.pdf (2.86 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-04289610 , version 1 (16-11-2023)

Identifiants

Citer

Theo Zurcher, Vincent Fridrici, Eric Charkaluk. Surface microstructure of an IN718 3D coating manufactured by Laser Metal Deposition. Materials Characterization, 2023, 203, pp.113054. ⟨10.1016/j.matchar.2023.113054⟩. ⟨hal-04289610⟩
29 Consultations
40 Téléchargements

Altmetric

Partager

Gmail Mastodon Facebook X LinkedIn More