Visible radiophotoluminescence of color centers in lithium fluoride thin films for high spatial resolution imaging detectors for hard X-rays
Résumé
Passive solid-state detectors based on the visible radiophotoluminescence (RPL) of stable aggregate F$_2$ and F$_3$$^+$ color centers in lithium fluoride (LiF) are successfully used for X-ray imaging and advanced diagnostics of intense X-rays sources. Among their advantages, these detectors offer a wide dynamic range and simplicity of use. They can be read non-destructively using a fluorescence microscope, enabling high spatial resolution over a large field of view. Optically transparent LiF films, of three different increasing thicknesses, were grown by thermal evaporation on glass and silicon substrates and subsequently irradiated with monochromatic 7 keV X-rays at several doses from 1.3 × 10$^1$ to 4.5 × 10$^3$ Gy at the SOLEIL synchrotron facility. For all the LiF films, the RPL response was found to depend linearly on the irradiation dose, with films grown on Si(100) substrates exhibiting up to a 50% higher response compared to those grown on glass. A minimum dose of 13 Gy was detected, despite the low thickness of the irradiated films. The limited thickness of the homogeneously colored LiF film allowed to obtain a spatial resolution of (0.44 ± 0.04) μm in edge-enhancement imaging experiments conducted by placing an Au mesh in front of the samples.
Domaines
Physique [physics]| Origine | Fichiers produits par l'(les) auteur(s) |
|---|