Improvement of thermal stability and flame retardancy of beech wood fibers using steam explosion and phosphorylation reaction - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Bioresources Année : 2023

Improvement of thermal stability and flame retardancy of beech wood fibers using steam explosion and phosphorylation reaction

Résumé

An environmentally friendly approach was studied for improving the fire retardancy of beech wood using a steam explosion process coupled with a phosphorylation reaction. Raw beech, steam-exploded, or bleached wood was subjected to phosphorylation employing etidronic acid (HEDP) and urea, and the resulting chemical composition and thermal behavior were analyzed using techniques such as elemental analysis, Fourier transform infrared spectroscopy, ionic chromatography, and pyrolysis combustion flow calorimetry. The thermal performance of beech wood underwent significant enhancements after the steam explosion treatment combined with soda impregnation. It resulted in a striking reduction in heat release rates (HRR), especially its peak (pHRR) and time-to-pHRR (TpHRR) values (from 139.5 W/g and 365 °C to 40 W/g and 247 °C) and an increase in residue from 10.5% to 41.3%. The results demonstrate that the process created a self-extinguishing and non-flammable material that exhibited noteworthy flame retardancy improvement.
Fichier principal
Vignette du fichier
BioRes_18_4_7309_Cheng_ZVZAJCLB_Improvem_Thermal_Beech_Fibers_Steam_22770.pdf (552.14 Ko) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte

Dates et versions

hal-04284619 , version 1 (14-11-2023)

Licence

Paternité

Identifiants

Citer

Liangsong Cheng, Tianyi Zhan, Henri Vahabi, Isabelle Ziegler-Devin, Karina Antoun, et al.. Improvement of thermal stability and flame retardancy of beech wood fibers using steam explosion and phosphorylation reaction. Bioresources, 2023, 18 (4), pp.7309 - 7319. ⟨10.15376/biores.18.4.7309-7319⟩. ⟨hal-04284619⟩
28 Consultations
20 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More