A Study of Temperature‐Dependent Photoluminescence from As‐Deposited and Heavy‐Ion‐Irradiated Plasma‐Enhanced Chemical Vapor Deposition‐Grown Si‐Rich a ‐SiN x :H Thin Films - HAL Accéder directement au contenu
Article dans une revue physica status solidi (b) Année : 2020

A Study of Temperature‐Dependent Photoluminescence from As‐Deposited and Heavy‐Ion‐Irradiated Plasma‐Enhanced Chemical Vapor Deposition‐Grown Si‐Rich a ‐SiN x :H Thin Films

Résumé

Temperature‐dependent photoluminescence (PL) measurements in the range of 10–300 K are carried out on silicon‐rich hydrogenated silicon nitride films deposited by plasma‐enhanced chemical vapor deposition. The in situ formation of Si quantum dots (QDs) with an average size of 3.5 nm is observed. The composition of thin films is estimated by Rutherford backscattering and ellipsometry. Broad PL spectra from thin films are decomposed into contributions from Si QDs, N dangling bonds (DBs), and Si DBs ( K ‐centers). At a low temperature, a strong PL can be observed, its quenching with increase in temperature is explained by the thermal activation of nonradiative decay mechanisms. Further, temperature‐dependent PL for swift heavy‐ion‐irradiated films shows similar quenching with increase in temperature. However, the effect of irradiation on the luminescence mechanisms of a ‐SiN x :H is revealed at low temperatures (<120 K) only, whereby a relatively narrow peak around 2.0 eV emerges. These results clearly show the role of radiative defects in the luminescence from Si‐rich silicon nitride.
Fichier principal
Vignette du fichier
maniscript PSSB.pdf ( 524.96 Ko ) Télécharger
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-04280241, version 1 (22-11-2023)

Identifiants

Citer

Harsh Gupta, Olivier Plantevin, Ravi Bommali, Santanu Ghosh, Pankaj Srivastava. A Study of Temperature‐Dependent Photoluminescence from As‐Deposited and Heavy‐Ion‐Irradiated Plasma‐Enhanced Chemical Vapor Deposition‐Grown Si‐Rich a ‐SiN x :H Thin Films. physica status solidi (b), 2020, 257 (5), pp.314001. ⟨10.1002/pssb.201900378⟩. ⟨hal-04280241⟩
8 Consultations
53 Téléchargements
Dernière date de mise à jour le 26/06/2024
comment ces indicateurs sont-ils produits

Altmetric

Partager

Gmail Facebook Twitter LinkedIn Plus