Parallel Aluminum‐Cobalt Oxide Nanosheet Arrays with High‐Temperature Ferromagnetism

Résumé

Abstract Parallel nanomaterials possess unique properties and show potential applications in industry. Whereas, vertically aligned 2D nanomaterials have plane orientations that are generally chaotic. Simultaneous control of their growth direction and spatial orientation for parallel nanosheets remains a big challenge. Here, a facile preparation of vertically aligned parallel nanosheet arrays of aluminum‐cobalt oxide is reported via a collaborative dealloying and hydrothermal method. The parallel growth of nanosheets is attributed to the lattice‐matching among the nanosheets, the buffer layer, and the substrate, which is verified by a careful transmission electron microscopy study. Furthermore, the aluminum‐cobalt oxide nanosheets exhibit high‐temperature ferromagnetism with a 919 K Curie temperature and a 5.22 emu g −1 saturation magnetization at 300 K, implying the potential applications in high‐temperature ferromagnetic fields.
Fichier non déposé

Dates et versions

hal-04278511 , version 1 (10-11-2023)

Identifiants

Citer

Leilei Chen, Rong Huang, Xiaoxing Ke, Jin Yu, Tiantian Zhang, et al.. Parallel Aluminum‐Cobalt Oxide Nanosheet Arrays with High‐Temperature Ferromagnetism. Small, 2023, 19 (38), ⟨10.1002/smll.202301513⟩. ⟨hal-04278511⟩
8 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More