Diode-pumped mode-locked Yb:Sc2SiO5 laser generating 38 fs pulses

Lulu Dong
  • Fonction : Auteur
Zhang-Lang Lin
  • Fonction : Auteur
Yichen Liu
  • Fonction : Auteur
Ge Zhang
  • Fonction : Auteur
Huang-Jun Zeng
  • Fonction : Auteur
Wen-Ze Xue
  • Fonction : Auteur
Shande Liu
Lihe Zheng
Liangbi Su
Xavier Mateos
Haifeng Lin
  • Fonction : Auteur
Valentin Petrov
Li Wang
Weidong Chen

Résumé

We report on sub-40 fs pulse generation from a Yb:Sc 2 SiO 5 laser pumped by a spatially single-mode fiber-coupled laser diode at 976 nm. A maximum output power of 545 mW was obtained at 1062.6 nm in the continuous-wave regime, corresponding to a slope efficiency of 64% and a laser threshold of 143 mW. A continuous wavelength tuning across 80 nm (1030 -1110 nm) was also achieved. Implementing a SESAM for starting and stabilizing the mode-locked operation, the Yb:Sc 2 SiO 5 laser delivered soliton pulses as short as 38 fs at 1069.5 nm with an average output power of 76 mW at a pulse repetition rate of ∼79.8 MHz. The maximum output power was scaled to 216 mW for slightly longer pulses of 42 fs, which corresponded to a peak power of 56.6 kW and an optical efficiency of 22.7%. To the best of our knowledge, these results represent the shortest pulses ever achieved with any Yb 3+ -doped rare-earth oxyorthosilicate crystal.
Fichier principal
Vignette du fichier
Revised Diode-pumped SESAM ML YbSc2SiO5 laser v2 Pavel.pdf (2.26 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-04209398 , version 1 (02-11-2023)

Identifiants

Citer

Lulu Dong, Zhang-Lang Lin, Pavel Loiko, Yichen Liu, Ge Zhang, et al.. Diode-pumped mode-locked Yb:Sc2SiO5 laser generating 38 fs pulses. Optics Express, 2023, 31 (8), pp.12463-12470. ⟨10.1364/OE.486560⟩. ⟨hal-04209398⟩
36 Consultations
9 Téléchargements

Altmetric

Partager

Gmail Mastodon Facebook X LinkedIn More