Wavelength tuning of InAs quantum dots grown on (311)B InP

Résumé

We report on the synthesis of InAs quantum dots on (311)B InP substrates. It is found that the use of such high index surfaces allows the formation of a high density (5×1010 islands/cm2) of small InAs islands (diameter≈350 Å) on InP. Moreover, a large improvement of the size uniformity is obtained in comparison with deposition on (100) surface. The standard height deviations are ±13% and ±50% for islands grown on (311)B and (100) surfaces, respectively. Then, we show that the modification of the As/P flux sequences, after the island formation, permits the control of the quantum dot emission wavelength. The achievement of quantum dots emitting at 1.55 μm at 300 K indicates that this method is promising for telecom device making.
Fichier non déposé

Dates et versions

hal-04175199 , version 1 (01-08-2023)

Identifiants

Citer

S. Fréchengues, N. Bertru, V. Drouot, B. Lambert, S. Robinet, et al.. Wavelength tuning of InAs quantum dots grown on (311)B InP. Applied Physics Letters, 1999, 74 (22), pp.3356-3358. ⟨10.1063/1.123343⟩. ⟨hal-04175199⟩
4 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More