Report of RILEM TC 281-CCC: effect of loading on the carbonation performance of concrete with supplementary cementitious materials — an interlaboratory comparison of different test methods and related observations - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Materials and structures Année : 2023

Report of RILEM TC 281-CCC: effect of loading on the carbonation performance of concrete with supplementary cementitious materials — an interlaboratory comparison of different test methods and related observations

Yan Yao
  • Fonction : Auteur correspondant
Ling Wang
  • Fonction : Auteur
Juan Li
  • Fonction : Auteur
  • PersonId : 1141949
Nele de Belie
  • Fonction : Auteur
  • PersonId : 1123689
Cheng Zhang
  • Fonction : Auteur
Visalakshi Talakokula
  • Fonction : Auteur
J Lu
  • Fonction : Auteur
Bin Li
  • Fonction : Auteur
Zhendi Wang
  • Fonction : Auteur
Yu Huang
  • Fonction : Auteur

Résumé

Durability of concrete with supplementary cementitious materials (SCMs) is crucial to the longevity of our built environment. Current research on the carbonation performance of concrete focuses on determining changes in microstructure induced by the chemical and physical interactions of CO2 with the cement phase in samples that do not undergo loading. Although this approach has enabled us to understand the chemical carbonation durability of concrete, the deterioration process is certainly not realistic considering the in-service conditions of structural concrete. Therefore, five different laboratories from RILEM TC 281-CCC WG4 conducted comparative testing of Portland cement concrete with/without SCMs under the combined action of carbonation and mechanical loading. The results indicated that the carbonation depth of concrete undergoing mechanical loading is lower in the case of a limited compressive load, and higher in the case of a high compressive load or tensile load, compared with unloaded specimens. The relative carbonation depth was decreased by 9–16% at 30% of the failure load in compression, independent of CO2 concentration and the presence of SCMs, while it was increased up to 13% at a 60% load level at most. Tension made the carbonation depth gradually increase, and up to 70% higher carbonation depth was reached at 60% of the tensile failure load. The combined effect of carbonation in concrete with SCMs and mechanical loading should therefore not be neglected in the service life prediction of concrete structures. © 2023, The Author(s), under exclusive licence to RILEM.
Fichier non déposé

Dates et versions

hal-04164422 , version 1 (18-07-2023)

Identifiants

Citer

Yan Yao, Ling Wang, Juan Li, Nele de Belie, Xinyu Shi, et al.. Report of RILEM TC 281-CCC: effect of loading on the carbonation performance of concrete with supplementary cementitious materials — an interlaboratory comparison of different test methods and related observations. Materials and structures, 2023, 56 (6), pp.110. ⟨10.1617/s11527-023-02190-0⟩. ⟨hal-04164422⟩
18 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More