Critical behavior near room temperature in La0.75Ca0.05Na0.20MnO3 sample

Résumé

The critical behavior of La0.75Ca0.05Na0.20MnO3 was studied at around room temperature via magnetization measurements. From the relative slope, we deduced that the Tricritical Mean-Field model was the most suitable model. The estimated critical exponents were found to be β = 0.24 ± 0.004, γ = 0.98 ± 0.065 and δ = 5.08 at TC = 300 K. These critical exponents satisfied the Widom scaling relation δ = 1 + γ/β, implying the reliability of our values. Based on the critical exponents, the magnetization–field–temperature (M–μ0H–T) data around TC collapsed into two curves, obeying the single scaling equation M(H,ε) = ε^β f±(H/(ε^β+γ) with ε = (T − TC)/TC being the reduced temperature. These results suggest short-range interaction in our sample.
Fichier principal
Vignette du fichier
c9ra00766k.pdf (1.56 Mo) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte

Dates et versions

hal-04149008 , version 1 (03-07-2023)

Identifiants

Citer

Souhir Bouzidi, Mohamed Amara Gdaiem, J. Dhahri, E.K. Hlil. Critical behavior near room temperature in La0.75Ca0.05Na0.20MnO3 sample. RSC Advances, 2019, 9 (24), pp.13808-13813. ⟨10.1039/C9RA00766K⟩. ⟨hal-04149008⟩

Collections

UGA CNRS NEEL
1 Consultations
6 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More