Optical and morphological properties of ZnO and Alq3 incorporated polymeric thin layers fabricated by the dip-coating method

Résumé

In this report, we present the influence of polymer matrix on morphological and optical properties of thin films containing zinc oxide (ZnO), tris(8-hydroxyquinolinato)aluminium (Alq 3 ) and ZnO:Alq 3 . Polyvinylpyrrolidone (PVP) and poly(methyl methacrylate) (PMMA) dissolved in isopropanol and tetrahydrofuran, respectively, were used as polymeric matrices of fabricated composites. The analysed thin layers were deposited on Si substrates using a dip-coating method and characterized by Fourier-Transform Infrared Spectroscopy (FTIR), Energy-Dispersive X-ray spectroscopy (EDX), Atomic Force Microscopy (AFM), Scanning Electron Microscopy (SEM), Spectroscopic Ellipsometry (SE) and photoluminescence (PL). It was found that adding the polymer to Alq 3 causes a blueshift in absorption compared to pure Alq 3 layers. We also observed photoluminescence in the region of 2.2–2.8 eV for ZnO:Alq 3 :PMMA and ZnO:Alq 3 :PVP, as well as for Alq 3 :PMMA at room temperature. PL measurements showed that adding ZnO to Alq 3 :polymer matrix did not result in any shift in PL spectra compared to the results of Alq 3 :polymer layer. AFM and SEM measurements show that relatively smooth films were obtained in the case of composites based on PVP and PMMA. Moreover, a change in the size of ZnO agglomerates depending on polymer used is observed for the three-component layers. We also noticed that the values of the refractive index are higher for the samples in the PVP matrix. However, the opposite behaviour was observed in the case of the extinction coefficient.
Fichier principal
Vignette du fichier
s13204-022-02647-8.pdf (2.45 Mo) Télécharger le fichier
Origine : Publication financée par une institution

Dates et versions

hal-04138823 , version 1 (21-03-2024)

Identifiants

Citer

M. Sypniewska, R. Szczesny, L. Skowronski, P. Kamedulski, E. Gondek, et al.. Optical and morphological properties of ZnO and Alq3 incorporated polymeric thin layers fabricated by the dip-coating method. Applied Nanoscience, 2023, 13 (7), pp.4903-4912. ⟨10.1007/s13204-022-02647-8⟩. ⟨hal-04138823⟩
12 Consultations
2 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More