Effect of build orientation and post-curing of (meth)acrylate‐based photocurable resin fabricated by stereolithography on the mechanical behavior from quasi-static to high strain rate loadings - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue International Journal of Advanced Manufacturing Technology Année : 2022

Effect of build orientation and post-curing of (meth)acrylate‐based photocurable resin fabricated by stereolithography on the mechanical behavior from quasi-static to high strain rate loadings

Résumé

Stereolithography (SLA) is becoming an important fabrication method among the different additive manufacturing techniques. This study investigates the effect of high strain rate on mechanical behavior, considering the fact that materials can be shown different mechanical properties under rapid straining compared to quasi-static loading. In addition, the role of polymerization as a determining factor in the final mechanical properties of the SLA parts is indicated. Regarding that, samples based on urethane dimethacrylate resin material were printed in different directions (θ = [0–90]) and post-treatment was performed with respect to the UV and UV with temperature. The effect of high strain rate was analyzed through a servo-hydraulic machine, monotonic, and interrupted tensile tests ranging from 0.3 to 117.4 s−1. Scanning electron microscopy was applied to analyze the failure surface characteristics. The results show the important effect of strain rate on mechanical properties such that by increasing the strain rate, yield stress and ultimate stress were increased. Furthermore, investigation of the strain rate sensitivity during the different steps of the failure indicates more sensitivity of the non-linear zone of the stress–strain curve with strain rate.
Fichier principal
Vignette du fichier
LCPI_IJAMT_2022_BENFRIHA.pdf (2.42 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03971062 , version 1 (03-02-2023)

Identifiants

Citer

Mohammadali Shirinbayan, Nader Zirak, Ouiza Saddaoui, Amrid Mammeri, Kamel Azzouz, et al.. Effect of build orientation and post-curing of (meth)acrylate‐based photocurable resin fabricated by stereolithography on the mechanical behavior from quasi-static to high strain rate loadings. International Journal of Advanced Manufacturing Technology, 2022, 123 (5-6), pp.1877-1887. ⟨10.1007/s00170-022-10336-7⟩. ⟨hal-03971062⟩
41 Consultations
48 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More