Characterization of microcracking of NCF composites under accelerated hygrothermal cycles: Influence of the stitching yarn and the style of biaxial NCF - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Composites Part A: Applied Science and Manufacturing Année : 2021

Characterization of microcracking of NCF composites under accelerated hygrothermal cycles: Influence of the stitching yarn and the style of biaxial NCF

Résumé

In this paper, an analysis of the evolution of microcracking of Non-Crimp Fabric (NCF) polymer matrix laminates under hygrothermal loading is presented. These composites are reinforced with biaxial NCF styles ([+45/-45], [0/90], etc.) and manufactured by Liquid Resin Infusion (LRI). The samples are subjected to accelerated hygrothermal cycles that cause microcracks in specific resin-rich areas (RRA). Three types of microcracks were found to occur in the heterogeneous morphology of NCF. An experimental method based on 2D microscopic observations was adapted for the characterization of microcracking in several NCF laminates. 3D tomographic X-ray observations were performed to investigate the propagation and location of microcracks in the NCF volume. The influence of humidity on microcracking was investigated. The impact of several parameters on microcracking was discussed, in particular the stitching yarn size and styles of biaxial NCF used in laminates.
Fichier principal
Vignette du fichier
Depot_HAL_Manuscript_Revision_Microcracking_NCF_JCOMA_20-2522_V3.pdf (3.22 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Licence : CC BY NC ND - Paternité - Pas d'utilisation commerciale - Pas de modification

Dates et versions

hal-04056938 , version 1 (03-04-2023)

Licence

Paternité - Pas d'utilisation commerciale - Pas de modification

Identifiants

Citer

A. Bezzou, Mael Péron, Pascal Casari, V. Singery, D. Ponsolle, et al.. Characterization of microcracking of NCF composites under accelerated hygrothermal cycles: Influence of the stitching yarn and the style of biaxial NCF. Composites Part A: Applied Science and Manufacturing, 2021, 149, pp.106507. ⟨10.1016/j.compositesa.2021.106507⟩. ⟨hal-04056938⟩
27 Consultations
14 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More