Solid solution evolution during mechanical alloying in Cu-Nb-Al compounds

Résumé

This work concerns the structural evolution of Cu 70 Nb 20 Al 10 (at%) alloy processed by mechanical alloying using a planetary ball mill in air atmosphere for different times (4 to 200 h). The morphological, structural, microstructural, and thermal behaviors of the alloy were investigated by scanning electron microscopy, energy-dispersive spectroscopy, X-ray diffraction, and differential scanning calorimetry. X-ray diffraction patterns were examined using the Rietveld refinement technique with the help of the MAUD software. A disordered FCC-Cu(Nb,Al) solid solution was formed after 8 h of milling. The crystallite size, microstrain, and lattice parameter were determined by the Rietveld method. With increasing milling time, the crystallite size of the final product-ternary-phase FCC-Cu(Nb,Al)-is refined to the nanometer scale, reaching 12 nm after 200 h. This crystallographic structure combines good mechanical strength and good ductility. An increase in microstrain and partial oxidation were also observed with increasing milling time.

Domaines

Matériaux
Fichier principal
Vignette du fichier
article pour HAL.pdf (1.44 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-04012376 , version 1 (02-03-2023)

Identifiants

Citer

Kaouther Zaara, Mahmoud Chemingui, Virgil Optasanu, Mohamed Khitouni. Solid solution evolution during mechanical alloying in Cu-Nb-Al compounds. International Journal of Minerals, Metallurgy, and Materials, 2019, 26 (9), pp.1129 - 1139. ⟨10.1007/s12613-019-1820-y⟩. ⟨hal-04012376⟩
4 Consultations
53 Téléchargements

Altmetric

Partager

Gmail Mastodon Facebook X LinkedIn More