Kinetics of iron electrochemical reduction into liquid metal at 1823 K in a molten oxide electrolyte - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Materials Chemistry and Physics Année : 2018

Kinetics of iron electrochemical reduction into liquid metal at 1823 K in a molten oxide electrolyte

Jan Wiencke
  • Fonction : Auteur correspondant
  • PersonId : 1232906

Connectez-vous pour contacter l'auteur
Hervé Lavelaine
  • Fonction : Auteur
Pierre-Jean Panteix
Carine Petitjean
Christophe Rapin

Résumé

The goal of this study was the measurement of the kinetic parameters of the electrochemical reduction of iron oxide into liquid iron metal in a molten oxide electrolyte, Al2O3-FeOx-MgO-SiO2, at 1823 K. A large surface anode was used to circumvent the need of a reference electrode and a stepped linear scan voltammetry was applied to an iron-bearing silicate electrolyte over a cell-voltage range of 0.8 V to 1.9 V. In order to extract the kinetic parameters the current response is treated concerning the electronic charge transfer and the ohmic drop due to the electrolyte in the electrochemical cell. The cathode half-reaction identified by this method is the reduction of ferrous iron into its metal state. Derived parameters imply that electrode kinetics follow Tafel behavior. An order of reaction close to unity with transfer coefficients between 0.54 and 0.66 is identified.

Domaines

Matériaux
Fichier principal
Vignette du fichier
MATCHEMPHYS-S-17-02245 HAL_removed.pdf (1.49 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-04010945 , version 1 (02-03-2023)

Identifiants

Citer

Jan Wiencke, Hervé Lavelaine, Gavin John Kane, Pierre-Jean Panteix, Carine Petitjean, et al.. Kinetics of iron electrochemical reduction into liquid metal at 1823 K in a molten oxide electrolyte. Materials Chemistry and Physics, 2018, 212, pp.214-223. ⟨10.1016/j.matchemphys.2018.03.020⟩. ⟨hal-04010945⟩
5 Consultations
14 Téléchargements

Altmetric