Mechanical Behavior Characterization of a Stainless Steel Dissimilar Metal Weld Interface : In-situ Micro-Tensile Testing on Carburized Martensite and Austenite - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Experimental Mechanics Année : 2020

Mechanical Behavior Characterization of a Stainless Steel Dissimilar Metal Weld Interface : In-situ Micro-Tensile Testing on Carburized Martensite and Austenite

Résumé

Stainless Steel Dissimilar Metal Welds (SS DMW) between low-alloy steel 18MND5 and austenitic 316L stainless steel are critical junctions in the currently operating reactors because of their heterogeneous microstructure and mechanical properties. The presence of a narrow hard layer of carburized martensite and austenite in the ferritic-austenitic interface creates an important hardness gradient which affects the crack behavior of the SS DMW. In order to evaluate the plastic properties of this hard layer, a micro tensile testing method was developed. Tensile specimens of 15 x 80 x 6 μm were extracted from the martensitic and carburized austenitic layers by focused ion beam (FIB) micro-processing and tested using an in-situ tensile testing device. A platinum FIB deposition was used to measure local strain in the specimen during the test through digital image correlation (DIC). Isotropic elasto-plastic constitutive laws for the martensite and carburized austenite were obtained from the true strain-stress curves calculated from the micro-tensile tests. It was found that the corresponding plastic properties were in a good agreement with nanoindentation measurements and with values obtained from macroscopic tensile tests on crossweld specimens machined perpendicularly to the ferritic-austenitic interface and characterized using laser beam local diameter measurements. In-situ tensile testing is a promising technique for plastic behavior characterization of small scale materials and local hard layers in dissimilar metal welds
Fichier principal
Vignette du fichier
BenSalem_ExpMech_2020.pdf (9.59 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03993144 , version 1 (03-08-2023)

Identifiants

Citer

G. Ben Salem, E. Héripré, P. Bompard, S. Chapuliot, A. Blouin, et al.. Mechanical Behavior Characterization of a Stainless Steel Dissimilar Metal Weld Interface : In-situ Micro-Tensile Testing on Carburized Martensite and Austenite. Experimental Mechanics, 2020, 60 (8), pp.1037-1053. ⟨10.1007/s11340-020-00633-1⟩. ⟨hal-03993144⟩
27 Consultations
14 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More